Hifax CA 207 A
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Hifax CA 207 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology. It is suitable for injection molding applications as well as for wire & cable extrusion process. As an impact modifier for compounding applications, it can be blended with other polyolefinic resins for a better shrinkage control and to improve the low temperature impact resistance. It does not contain any slip nor anti-blocking agents. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高冲击耐低温冲击耐热耐磨尺寸稳定 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑线缆挤出共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.89 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 7.5 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 14 Mpa | ISO 527-1/-2 | |
断裂(brk) | 22 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 20 % | ISO 527-1/-2 | |
断裂(brk) | 700 % | ISO 527-1/-2 | |
弯曲模量 | 550 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 5 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 45 kJ/m2 | ISO 179 | Partial Break |
23℃ (73℉) | 65 kJ/m2 | ISO 179 | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 46 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 58 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 94 °C | ISO 306/A50 | |
熔融温度(Tm) | 163 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 23 % | ASTM D1003 | 45 μm |
雾度 | 13 % | ASTM D1003 | 50 μm |
光泽度 | 60 - | ASTM D 2457 | 45°, 50 μm |
光泽度 | 110 - | ASTM D 2457 | 60°, 45 mil |