Hifax CA 387 A
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Hifax CA 387 A is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It has high melt flow and an excellent balance of impact, stiffness, processability and paintability. Hifax CA 387 A is primarily used for painted automotive bumper fascias that require high durability, and for other injection molded parts with paintable and weatherable requirements. It is also utilized as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性高耐久性阻燃颜色稳定/易着色易涂装易脱模耐候性高流动 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.89 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 18.5 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 18 Mpa | ISO 527-1/-2 | |
断裂(brk) | 13 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-1/-2 | |
断裂(brk) | 110 % | ISO 527-1/-2 | |
弯曲模量 | 1000 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 2.6 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 8.7 kJ/m2 | ISO 179 | Complete Break |
23℃ (73℉) | 60 kJ/m2 | ISO 179 | Partial Break |
多轴冲击 | 27 J | ASTM D3763 | -40°C, 3.20 mm, Ductile Failure |
多轴冲击 | 17 J | ASTM D3763 | 23°C, 3.20 mm, Ductile Failure |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 52 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 80 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 120 °C | ISO 306/A50 | |
熔融温度(Tm) | 163 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
光泽度 | 77 - | ASTM D 2457 | 60°, 45 mil |