Plexiglas® V045i
PMMA(亚克力)
阿科玛Altuglas (Arkema)
产品描述
Plexiglas® V045i is a lightly impact modified thermoplastic acrylic resin formulated for extrusion applications. It is characterized by its chemical and heat resistance as well a high melt flow. It is a tougher resin than Plexiglas® V045 allowing improved fabrication. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics.
基本信息
| 原厂资料 | 物性表-ASTM(英文) 宣传册 (英文) | |||
| 产品特性 | 高冲击高韧性耐热抗紫外线耐候性耐化学性高流动 | |||
| 添加助剂 | 抗冲击剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.19 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 2.1 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.2~0.6 % | ASTM D 955 | |
吸水率 | 0.3 % | ASTM D570 | 24 hr immersion |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 67.6 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 15 % | ASTM D638 | |
弯曲强度 | |||
断裂(brk) | 98.6 Mpa | ASTM D790 | |
弯曲模量 | 2930 Mpa | ASTM D790 | |
拉伸模量 | 2960 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 21 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 89 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 92.2 °C | ASTM D648 | annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 90.6 °C | ASTM D648 | annealed |
维卡软化温度(Vicat) | 101 °C | ASTM D1525 | 50°C/hr; 10N |
维卡软化温度(Vicat) | 92.2 °C | ASTM D1525 | 50°C/hr; 50N |
导热系数 | 0.19 W/(m K) | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | ASTM D 635 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ASTM D1003 | 3.2 mm |
雾度 | 1 % | ASTM D1003 | 3.2 mm |
折射率 | 1.49 - | ASTM D542 | Nd @ 72°F |