PLEXIGLAS® Resist zk5BR
PMMA(亚克力)
罗姆化学(原赢创)(Rohm/Roehm Chemical)
产品描述
PLEXIGLAS® Resist zk5BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
Typical properties of impact-modified PLEXIGLAS® molding compounds are:
• high weather resistance
• excellent transmission and clarity
• brilliant appearance
• the pleasant feel and sound of the moldings.
PLEXIGLAS® Resist zk5BR is characterized by the following special properties:
• high break resistance and impact strength
• improved resistance to stress cracking
• balanced property profile
• AMECA listing.
Application:
Used for injection molding as well as for extruding and coextruding panels and profiles
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性透光良好表面耐候性 | |||
| 添加助剂 | 抗冲击剂 | |||
| 法规认证 | AMECA(美国加拿大汽车认证) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出片材挤出型材挤出共挤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.17 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 3.3 cm³/10 min | ISO 1133 | |
吸水率 | 1.9 % | ISO 62 | saturation, 23°C |
吸湿率 | 0.5 % | ISO 62 | 23°C / 50% |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4.5 % | ISO 527 | 50 mm/min |
标称断裂伸长率 | 27 % | ISO 527 | |
拉伸模量 | 2400 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 50 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 98 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 93 °C | ISO 75 | |
维卡软化温度(Vicat) | 100 °C | ISO 306/B50 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 90 E-6/K | ISO 11359 | 0-50 °C |
玻璃化温度(Tg) | 109 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ISO 13468-2 | 3mm, D65 |
雾度 | 2 % | ASTM D1003 | 3mm |
折射率 | 1.49 - | ISO 489 | 3mm, 589nm/23°C |