KetaSpire® KT-810

KetaSpire® KT-810

KetaSpire® KT-810

PEEK(聚醚醚酮)

索尔维(苏威)(Solvay)

产品描述

KetaSpire® KT-810 is an ultra-high molecular weight natural PEEK resin having a melt viscosity ranging from 0.51-0.65 kPa-s as compared to 0.38-0.50 kPa-s for standard high-viscosity PEEK grades such as KT-820. KetaSpire PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent chemical resistance to organics, acids and bases; exceptional retention of mechanical properties up to 240°C (464°F); best-in-class fatigue resistance; excellent wear resistance; ease of melt processing; and high purity. The KT-810 grade achieves a greater level of mechanical toughness than previously possible with PEEK, yet it is still processable by conventional methods including extrusion, injection molding, and compression molding.

KetaSpire® KT-810 is particularly suited for compression molding applications such as machined parts and stock shapes wherein the inherent slow cooling rates of the process limit PEEK's toughness and often result in brittleness due to the higher crystallinity levels.

The grade is available in two forms: fine powder with average particle size of approximately 50 micrometers (µm) for compression molding, and pellet form for extrusion and injection molding. The fine powder grade is designated KT-810FP while the pelletized product is available as KT-810 NT.

  • Fine Powder: KT-810 FP

  • Natural Pellet: KT-810 NT

    基本信息
    原厂资料
    物性表(英文)
    产品特性
    耐疲劳
    高冲击
    高韧性
    耐热
    阻燃
    电子束灭菌
    耐伽马射线
    环氧乙烷灭菌(EtO)
    耐蒸煮
    耐化学性
    添加助剂
    润滑剂
    法规认证
    ISO10993(生物相容性)
    MIL P-46183(美国军用标准)
    颜色形状
    粒状
    粉末状
    本色
    成型方式
    注塑
    挤出
    片材挤出
    吹塑
    热成型
    模压
    技术参数
    物理性能 值/单位 测试标准 测试条件

    比重

    1.29 - ASTM D792

    吸水率

    0.1 % ASTM D570
    24 hr

    粘度

    510~650 Pa-s ASTM D 3835
    400℃,1000 sec-1
    机械性能 值/单位 测试标准 测试条件

    拉伸强度

    屈服(yld)

    94.5 Mpa ASTM D638
    50 mm/min

    拉伸延伸率

    屈服(yld)

    5.2 % ASTM D638
    50 mm/min

    断裂(brk)

    85 % ASTM D638
    5.0 mm/min

    断裂(brk)

    25~50 % ASTM D638
    50 mm/min

    弯曲强度

    -

    145 Mpa ASTM D790

    弯曲模量

    3700 Mpa ASTM D790

    拉伸模量

    3500 Mpa ASTM D638
    50 mm/min
    冲击性能 值/单位 测试标准 测试条件

    悬臂梁缺口(Izod Notched)

    -

    100 J/m ASTM D 256

    悬臂梁无缺口(Izod Unnotched)

    -

    NB J/m ASTM D 4812
    热学性能 值/单位 测试标准 测试条件

    热变形温度(HDT)

    1.8 Mpa (264 psi)(18.6kg/cm²)

    157 °C ASTM D648
    Annealed