VICTREX® PEEK 90G
PEEK(聚醚醚酮)
威格斯(Victrex)
产品描述
High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige.
Typical Application Areas:
Complex geometries with thinner cross sections or longer flow lengths, for high strength and stiffness as well as good ductility.
Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 食品接触级医疗级耐化学性高流动 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状本色米色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.3 g/cm³ | ISO 1183 | Crystalline |
收缩率 | |||
纵向(Flow) | 1 % | ISO 294-4 | Along flow |
横向(Across Flow) | 1.3 % | ISO 294-4 | Across flow |
吸水率 | 0.55 % | ISO 62-1 | Saturation, 100°C, by immersion |
吸水率 | 0.45 % | ISO 62-1 | Saturation, 23°C, by immersion |
粘度 | 90 Pa-s | ISO 11443 | Melt Viscosity, 400°C |
螺旋流 | 245 mm | - | 365°C nozzle, 160°C tool, 1mm thick |
螺旋流 | 280 mm | - | 375°C nozzle, 180°C too, 1mm thick |
螺旋流 | 330 mm | - | 400°C nozzle, 200°C tool, 1mm thick |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 105 Mpa | ISO 527 | 23°C |
拉伸延伸率 | |||
断裂(brk) | 20 % | ISO 527 | 23°C |
弯曲强度 | |||
屈服(yld) | 175 Mpa | ISO 178 | 23°C |
3.5%应变 | 130 Mpa | ISO 178 | 23°C |
- | 90 Mpa | ISO 178 | 125°C |
- | 20 Mpa | ISO 178 | 175°C |
- | 13.5 Mpa | ISO 178 | 275°C |
弯曲模量 | 3900 Mpa | ISO 178 | 23°C |
拉伸模量 | 4100 Mpa | ISO 527 | 23°C |
抗压强度 | 80 Mpa | ISO 604 | 120°C |
抗压强度 | 130 Mpa | ISO 604 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/U | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 4.5 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 180/U | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 85 D | ISO 868 | 23°C |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 167 °C | ISO 75/Af | Annealed 200°C / 4h |
1.8 Mpa (264 psi)（18.6kg/cm²） | 156 °C | ISO 75/Af | As moulded |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 120 E-6/K | ISO 11359 | Along flow above 143°C |
纵向(Flow) | 50 E-6/K | ISO 11359 | Along flow below 143°C |
横向(Across Flow) | 140 E-6/K | ISO 11359 | Average above 143°C |
横向(Across Flow) | 55 E-6/K | ISO 11359 | Average below 143°C |
熔融温度(Tm) | 343 °C | ISO 11357 | |
玻璃化温度(Tg) | 143 °C | ISO 11357 | Onset |
导热系数 | 0.32 W/(m K) | ISO 22007-4 | Along flow, 23°C |
导热系数 | 0.29 W/(m K) | ISO 22007-4 | Average, 23°C |
加工温度 | 350~360 °C | - | |
模具温度 | 160~200 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
灼热丝可燃性指数(GWFI) | |||
2mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | 125°C |
体积电阻率 | 1.0E+16 Ohm-cm | IEC 60093 | 23°C |
体积电阻率 | 1.0E+9 Ohm-cm | IEC 60093 | 275°C |
介电常数(DK) | |||
1 kHz | 3.1 - | IEC 60250 | 23°C |
耗散因数(DF) | |||
1MHz | 40 E-4 | IEC 60250 | 23°C |
相比漏电起痕指数(CTI ) | |||
- | 150 V | IEC 60112 | |
绝缘强度 | 23 kV/mm | IEC 60243-1 | 2mm thickness |