LEXAN™ 505RU
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN 505RU Polycarbonate (PC) is an injection moldable non-chlorinated and non-brominated flame retardant grade that is 10% glass fiber filled. It It is UV stabilized and has a UL94 V0@1.5mm rating and is available in various opaque color options. This is an alternative to LEXAN 503R, 503R, 503RS.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无氯无溴抗紫外线填充增强 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 颜色形状 | 不透明色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 10% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.26 g/cm³ | ISO 1183 | |
比重 | 1.26 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 7 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 8 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.6 % | Internal | flow, 3.2 mm |
吸水率 | 0.3 % | ISO 62 | 23°C/sat |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 74 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 72 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 60 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 62 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 3 % | ISO 527 | 5 mm/min |
断裂(brk) | 6 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 6 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 114 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 122 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 3200 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3500 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 3600 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 3500 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 70 J/m | ASTM D256 | |
-30℃ (-22℉) | 8 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 90 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 73 kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | 1200 J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 25 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 137 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 149 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 149 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 147 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 50 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 50 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 74 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 85 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | Pass |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.75 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
5VB | 3 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.0mm | 850 °C | IEC 60695-2-13 | |
3.0mm | 875 °C | IEC 60695-2-13 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 175 V | IEC 60112 | |
- | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 3 PLC | UL 746A | |
高电流弧起燃性(HAI) | 0 PLC | UL 746A |