EMERGE™ PC 8430-7 LT
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8430-7 LT advanced resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and high RTI properties, ensuring longer sustained aesthetics and mechanical resistance, to the applications. EMERGE ™ PC 8430-7 LT has a UL 94 V-0 rating at 1.5 mm, and contains mould release agent and UV stabilizer.
Applications:
Electrical
Lighting
Diffusers
Lenses
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 阻燃无氯无溴无红磷易脱模抗紫外线 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂脱模剂 | |||
| 法规认证 | VDE/DIN 472 | |||
| 颜色形状 | 粒状透明 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 7 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 70 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 110 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 95 Mpa | ISO 178 | |
弯曲模量 | 2350 Mpa | ISO 178 | |
拉伸模量 | 2400 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 35 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 70 kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 144 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 141 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 148 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6 cm/cm/℃ | ISO 11359-2 | |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.75 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
氧指数(LOI) | 40 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
2mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
2.0mm | 800 °C | IEC 60695-2-13 | |
3.0mm | 800 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
介电常数(DK) | |||
1 Hz | 2.7 - | IEC 60250 | |
50 Hz | 2.7 - | IEC 60250 | |
耗散因数(DF) | |||
1 Hz | 10 E-4 | IEC 60250 | |
50 Hz | 10 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
溶液A | 225 V | IEC 60112 | |
绝缘强度 | 17 kV/mm | IEC 60243-1 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88~89 % | ASTM D1003 |