CALIBRE™ 5201-8
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-8 resin is typically used in electrical market applications. CALIBRE 5201-8 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.
Main Characteristics:
Glass reinforced
Ignition resistant
Tested under ISO 10993
Applications:
Electrical boxes
Lighting components
Electrical connectors
Medical applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃尺寸稳定易脱模医疗级生物相容填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 法规认证 | ISO10993(生物相容性) | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
密度 | 1.36 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 8 g/10min | ASTM D1238 | |
300℃/1.2 kg | 8 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.2~0.4 % | ASTM D 955 | |
纵向(Flow) | 0.2~0.4 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 82.7 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 83 Mpa | ISO 527-2/50 | |
断裂(brk) | 82.7 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 83 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 2.6 % | ASTM D638 | 50 mm/min |
屈服(yld) | 2.6 % | ISO 527-2/50 | |
断裂(brk) | 3 % | ASTM D638 | 50 mm/min |
断裂(brk) | 3 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 148 Mpa | ASTM D790 | 2.0 mm/min |
- | 148 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 4830 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 4820 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 5170 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 5170 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 110 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 46.3 J | ASTM D3763 | 3.39 m/sec |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 122 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 148 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 148 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 142 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 138 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 142 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 138 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 159 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 158 °C | ISO 306/B50 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 1.6 mm | UL94 | |
V-0 | 3 mm | UL94 |