Lexan* FST9405 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.583 compliant and an ideal candidate foraircraft interior applications. Available in opaque colors.
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.33 g/cm³
| ISO 1183 | |
比重 | 1.33 -
| ASTM D792 | |
熔体体积流动速率(MVR) | | | |
300°C/1.2 kg |
10 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
9 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.5~0.7 % | Internal | |
横向(Across Flow) |
0.5~0.7 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
77 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
77 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
70 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
70 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
6 % | ISO 527 | 50 mm/min |
断裂(brk) |
75 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
95 % | ISO 527 | 50 mm/min |
弯曲强度 | | | |
屈服(yld) |
115 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) |
105 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2700 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2500 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 2600 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 2600 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
85 J/m | ASTM D256 | |
-30℃ (-22℉) |
9 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) |
130 J/m | ASTM D256 | |
23℃ (73℉) |
12 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) |
11 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) |
NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
60 J | ASTM D3763 | |
多轴冲击 | 130 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
105 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
104 °C | ISO 75-2/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
95 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
94 °C | ISO 75-2/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 114 °C
| ASTM D1525 | B/50 |
维卡软化温度(Vicat) | 113 °C
| ISO 306 | Rate B/120 |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
60 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) |
60 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
NBS 烟密度 | 75 -
| ASTM E 662 | Flaming, Dmax |
垂直燃烧 | 1 sec
| FAR 25.853 | 60s, passes at |
放热率 | 55 kW/m²
| FAR 25.853 | OSU peak, 5 minute test |
放热率 | 55 kW-min/m²
| FAR 25.853 | OSU total, 2 minute test |