Vydyne® 66B
PA66
奥升德(Ascend)
产品描述
Vydyne 66B is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66B resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性高韧性耐化学性耐燃油耐油耐溶剂高粘度高熔体强度 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)FED L-P-410AMIL M-20693B(美国军用标准)NSF(美国卫生基金会食品认证)RoHS(欧盟电子电气设备中有害物质)USDA(美国农业部有机认证) | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 2.1 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 2 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 8.5 % | ISO 62 | 24 hr, 23°C |
吸水率 | 2.5 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ISO 527-2 | Conditioned, 23°C |
屈服(yld) | 85 Mpa | ISO 527-2 | Dry, 23°C |
断裂(brk) | 70 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 55 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
屈服(yld) | 20 % | ISO 527-2 | Conditioned, 23°C |
屈服(yld) | 5 % | ISO 527-2 | Dry, 23°C |
标称断裂伸长率 | 150 % | ISO 527-2 | Conditioned, 23°C |
标称断裂伸长率 | 25 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 30 Mpa | ISO 178 | Conditioned, 23°C |
- | 90 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 900 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 3100 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 1800 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 2800 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.42 - | ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | Conditioned |
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 23 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Conditioned |
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | 6 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 25 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 6 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 195 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | |||
冲击w/impact,0.71mm | 75 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm | 75 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm | 75 °C | UL 746 | Dry |
电气Elec,0.71mm | 130 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm | 130 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm | 130 °C | UL 746 | Dry |
强度w/o impact,0.71mm | 85 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm | 85 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm | 85 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.71 mm | UL94 | Dry |
HB | 1.5 mm | UL94 | Dry |
V-2 | 3 mm | UL94 | Dry |
氧指数(LOI) | 28 % | ISO 4589 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.71mm | 850 °C | IEC 60695-2-12 | Dry |
1.5mm | 850 °C | IEC 60695-2-12 | Dry |
3mm | 960 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
0.71mm | 700 °C | IEC 60695-2-13 | Dry |
1.5mm | 700 °C | IEC 60695-2-13 | Dry |
3.0mm | 700 °C | IEC 60695-2-13 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 26 kV/mm | IEC 60243 | Dry, 1.00 mm |
耐电弧性 | 5 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.71 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 2 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 0.71 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 3.00 mm |