LNP™ THERMOCOMP™ RC004SXS
LNP™ THERMOCOMP™ RC004SXS
PA66
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP RC004SXS is a compound based on Nylon 66 containing 20% Carbon Fiber. Added feature of this grade includes: Heat Stabilized,Electrically Conductive.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 热稳定导电填充增强 |
| 添加助剂 | 热稳定剂 |
| 增强填充 | 20% 碳纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.23 g/cm³
| ISO 1183 | |
比重 | 1.23 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.2~0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
0.9~2 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 1.2 %
| ISO 62 | 23°C / 50% RH |
吸湿率 | 0.89 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
242 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
222 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
2.2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
2.5 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
断裂(brk) |
348 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
331 Mpa | ISO 178 | |
弯曲模量 | 13700 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 12920 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 16680 Mpa
| ASTM D638 | 50 mm/min |
拉伸模量 | 16740 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
67 J/m | ASTM D256 | |
23℃ (73℉) |
6 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
884 J/m | ASTM D4812 | |
23℃ (73℉) |
49 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
6 J | ASTM D3763 | |
多轴冲击 | 2 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
260 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
260 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
252 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
249 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
2.1E+7 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) |
9.0E+7 E-6/°C | ASTM D 696 | -30°C to 30°C, xflo |