Ultramid® B3WG7 BK00564
PA6
巴斯夫 (BASF)
产品描述
Ultramid B3WG7 BK00564 is a 35% glass fiber reinforced, pigmented black, injection molding PA6 grade for highly rigid, dimensionally stable components which are resistant to high temperature aging and have improved retention of properties in a hot water environment.
Applications
Typical applications include automotive clutch and accelerator pedals.
基本信息
原厂资料 | 物性表-ISO(英文) | |||
产品特性 | 高刚性耐热老化尺寸稳定耐水解填充增强 | |||
颜色形状 | 粒状黑色 | |||
成型方式 | 注塑 | |||
增强填充 | 35% 玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
吸水率 | 2 % | ISO 62 | 50% RH |
吸水率 | 6.2 % | ISO 62 | Saturation |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 188 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527 | Dry,23℃ |
弯曲模量 | 10000 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 11000 Mpa | ISO 527 | Dry,23℃ |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 180 | Dry |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | 215 °C | ISO 75 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+10 Ohm-m | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
介电常数(DK) | |||
1MHz | 6.2 - | IEC 60250 | Conditioned |
1MHz | 3.9 - | IEC 60250 | Dry |
耗散因数(DF) | |||
100Hz | 1900 E-4 | IEC 60250 | Conditioned |
100Hz | 210 E-4 | IEC 60250 | Dry |
1MHz | 1900 E-4 | IEC 60250 | Conditioned |
1MHz | 210 E-4 | IEC 60250 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 450 V | IEC 60112 | Conditioned |
- | 450 V | IEC 60112 | Dry |