DOWLEX™ SC 2106G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ SC 2106G is processable at high line speeds. Films made from DOWLEX SC 2106G Polyethylene Resin exhibit excellent stretchability, tear and impact resistance, as well as exceptional optical properties.
Applications:
Cast stretch wrap film
Main Characteristics:
Linear Low Density Polyethylene
Complies with:
U.S. FDA FCN 424
EU, No 10/2011
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 成型方式 | 流延薄膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.917 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 3.3 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
加工温度 | 220~280 °C | - | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 0.6 % | ASTM D1003 | 23 µm |
光泽度 | 93 - | ASTM D 2457 | 45°, 23 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6.2 Mpa | ASTM D 882 | MD, 23 µm |
屈服(yld) | 5.5 Mpa | ASTM D 882 | TD, 23 µm |
断裂(brk) | 38 Mpa | ASTM D 882 | MD, 23 µm |
断裂(brk) | 21 Mpa | ASTM D 882 | TD, 23 µm |
拉伸延伸率 | |||
断裂(brk) | 500 % | ASTM D 882 | MD, 23 µm |
断裂(brk) | 780 % | ASTM D 882 | TD, 23 µm |
埃尔曼多夫撕裂 | 320 g | ASTM D 1922 | MD, 23 µm |
埃尔曼多夫撕裂 | 530 g | ASTM D 1922 | TD, 23 µm |
落锤冲击 | 140 g | ASTM D 1709 | 23 µm |