DOWLEX™ 2045
LLDPE
陶氏化学(Dow Chemical)
产品描述
Linear Low Density Polyethylene
For heavy duty film applications
Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a.
Canadian HPFB No Objection (With Limitations)
EU, No 10/2011
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局) | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm³ | ASTM D792 | |
密度 | 0.92 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 108 °C | ASTM D1525 | |
熔融温度(Tm) | 122 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 9 % | ASTM D1003 | 20.3 µm |
雾度 | 10 % | ASTM D1003 | 50.8 µm |
光泽度 | 63 - | ASTM D 2457 | 45°, 20.3 µm |
光泽度 | 60 - | ASTM D 2457 | 45°, 50.8 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11.8 Mpa | ASTM D 882 | MD, 20 µm |
屈服(yld) | 10.9 Mpa | ASTM D 882 | MD, 51µm |
屈服(yld) | 12.1 Mpa | ASTM D 882 | TD, 20 µm |
屈服(yld) | 12.3 Mpa | ASTM D 882 | TD, 51 µm |
断裂(brk) | 64.2 Mpa | ASTM D 882 | MD, 20 µm |
断裂(brk) | 55.1 Mpa | ASTM D 882 | MD, 51µm |
断裂(brk) | 52.7 Mpa | ASTM D 882 | TD, 20 µm |
断裂(brk) | 49.8 Mpa | ASTM D 882 | TD, 51 µm |
拉伸延伸率 | |||
断裂(brk) | 640 % | ASTM D 882 | MD, 20 µm |
断裂(brk) | 830 % | ASTM D 882 | MD, 51µm |
断裂(brk) | 880 % | ASTM D 882 | TD, 20 µm |
断裂(brk) | 890 % | ASTM D 882 | TD, 51 µm |
耐穿透性 | 22.2 J/cm³ | Internal | 20 µm |
耐穿透性 | 19.4 J/cm³ | Internal | 51 µm |
抗拉韧性 | 319 J/cm³ | ASTM D882 | MD, 20 µm |
抗拉韧性 | 346 J/cm³ | ASTM D882 | MD, 51µm |
抗拉韧性 | 356 J/cm³ | ASTM D882 | TD, 20 µm |
抗拉韧性 | 351 J/cm³ | ASTM D882 | TD, 51 µm |
埃尔曼多夫撕裂 | 230 g | ASTM D 1922 | MD, 20 µm |
埃尔曼多夫撕裂 | 900 g | ASTM D 1922 | MD, 51µm |
埃尔曼多夫撕裂 | 520 g | ASTM D 1922 | TD, 20 µm |
埃尔曼多夫撕裂 | 1200 g | ASTM D 1922 | TD, 51 µm |
割线模量 | 210 Mpa | ASTM D 882 | 2% Secant, MD, 20 µm |
割线模量 | 194 Mpa | ASTM D 882 | 2% Secant, MD, 51 µm |
割线模量 | 232 Mpa | ASTM D 882 | 2% Secant, TD, 20 µm |
割线模量 | 233 Mpa | ASTM D 882 | 2% Secant, TD, 51 µm |
落锤冲击 | 150 g | ASTM D 1709 | 20 µm |
落锤冲击 | 290 g | ASTM D 1709 | 51 µm |