POLYAXIS® LL 3568
LLDPE
利安德巴塞尔(LyondellBasell)
产品描述
PolyAxis LL 3568 is a linear low density polyethylene intended for the rotational molding industry. Offers excellent ESCR and toughness.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高韧性抗紫外线ESCR | |||
| 颜色形状 | 粉末状可定制色 | |||
| 成型方式 | 滚塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.934 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 6.8 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 50 Hours | ASTM D 1693 | 10% Igepal, Compression Molded, F50 |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | 100% Igepal, Compression Molded, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 15.9 Mpa | ASTM D638 | 51 mm/min, Rotational Molded |
拉伸延伸率 | |||
屈服(yld) | 10 % | ASTM D638 | 50 mm/min, Rotational Molded |
弯曲模量 | 572 Mpa | ASTM D790 | 1% Secant, Rotational Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 79 J | Internal | -40°C, 3.18 mm, Rotational Molded |
落锤冲击 | 200 J | Internal | -40°C, 6.35 mm, Rotational Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 52.2 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 36.1 °C | ASTM D648 | Unannealed |
熔融温度(Tm) | 126 °C | ASTM D3418 | Peak Melting Temperature |