DOWLEX™ NG 5066G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ NG 5066G Polyethylene Resin is an ethylene octene-1 copolymer suitable for the production of blown film requiring good tear strength and outstanding toughness with good stiffness and temperature resistance. Typical application of use include lamination film.
Applications:
High clarity tissue overwrap
Produce bags
Food packaging films
Lamination film
Complies with:
EU, No 10/2011
U.S. FDA 21 CFR 177.1520(c)3.2a
Canadian HPFB No Objection
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局) | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.934 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1.7 g/10min | ISO 1133 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 124 °C | ASTM D1525 | |
加工温度 | 190~240 °C | - | Extrusion |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 14 Mpa | ISO 527-3 | MD, 50 µm |
屈服(yld) | 17 Mpa | ISO 527-3 | TD, 50 µm |
断裂(brk) | 21 Mpa | ISO 527-3 | MD, 50 µm |
断裂(brk) | 23 Mpa | ISO 527-3 | TD, 50 µm |
拉伸延伸率 | |||
断裂(brk) | 590 % | ISO 527-3 | MD, 50 µm |
断裂(brk) | 620 % | ISO 527-3 | TD, 50 µm |
拉伸模量 | 420 Mpa | ISO 527-3 | 2% Secant, MD, 50 µm |
拉伸模量 | 470 Mpa | ISO 527-3 | 2% Secant, TD, 50 µm |
埃尔曼多夫撕裂 | 130 g | ASTM D 1922 | MD, 50 µm |
埃尔曼多夫撕裂 | 230 g | ASTM D 1922 | TD, 50 µm |
落锤冲击 | 110 g | ISO 7765-1 | 50 µm |