中国YS FTa-1冶金用钽粉及机械属性、化学成分、对照参考.
数据表：金属：FTa-1 /FTa-1
FTa-1属性
| 类别 | 型号 | 标准 | 区域/地区 | 标准内容 |
|---|---|---|---|---|
| 金属 | FTa-1 | YS/T 259 | 中国 | 冶金用钽粉 |
FTa-1化学成分
FTa-1的化学成分（质量分数）（wt.%）
| 成分 | 最小值 | 最大值 | 类似 |
|---|---|---|---|
| P | - | 0.0015 | - |
| 镁 | - | 0.0010 | - |
| Cu | - | 0.0010 | - |
| Al | - | 0.0010 | - |
| 钙 | - | 0.0010 | - |
| 锡 | - | 0.0010 | - |
| Mn | - | 0.0010 | - |
| Ti | - | 0.0010 | - |
| Mo | - | 0.0010 | - |
| W | - | 0.0020 | - |
| NB | - | 0.0030 | - |
| Si | - | 0.0030 | - |
| Cr | - | 0.0030 | - |
| Ni | - | 0.0030 | - |
| Fe | - | 0.0030 | - |
| N | - | 0.0050 | - |
| C | - | 0.0050 | - |
| O | - | 0.1500 | - |
| H | - | 0.0030 | - |
| Ta | 99.9500 | - | - |
| Cr | - | 0.0050 | - |
| Mn | - | 0.0010 | - |
| Mo | - | 0.0020 | - |
| W | - | 0.0030 | - |
| Ti | - | 0.0010 | - |
| Si | - | 0.0150 | - |
| Ni | - | 0.0050 | - |
| Fe | - | 0.0050 | - |
| C | - | 0.0150 | - |
| N | - | 0.0080 | - |
| H | - | 0.0050 | - |
| O | - | 0.2000 | - |
| NB | - | 0.0100 | - |
FTa-1钢级机械属性
钢种的机械属性FTa-1
| 屈服强度 Rp0.2 (MPa) |
拉伸强度 Rm (MPa) |
冲击性能 KV/Ku (J) | 伸长率 A (%) |
断裂横截面减少 Z (%) |
热处理状态 | 布氏硬度 (HBW) |
|---|---|---|---|---|---|---|
| 623（≥） | 582（≥） | 14 | 42 | 12 | 固溶和老化、退火、Ausaging、Q+T等 | 331 |
物理属性
钢种的物理属性FTa-1
| 温度 (°C) |
弹性模量 (GPa) |
20(°C) 至 之间的平均热膨胀系数 10-6/(°C) | 导热系数 (W/m·°C) |
比热容 (J/kg·°C) |
比电阻电阻率 (Ω mm2/m) |
密度 (kg/dm3) |
泊松系数，ν |
|---|
| 23 | - | - | - | - | 0.22 | - | - |
| 652 | 932 | - | 32.3 | 233 | - | - | - |
| 877 | - | 33 | 44.2 | - | - | 112 | 214 |
热处理
钢种的热处理FTa-1
热处理：1331°C - 1534°C
技术曲线钢种工艺曲线FTa-1