Estane® 2103-55D TPU
TPU(热塑性聚氨酯)
路博润 (Lubrizol)
产品描述
Type: Estane® 2103-55D is a thermoplastic polyurethane elastomer.
Feature: Load bearing capacity.
基本信息
| 原厂资料 | 物性表(英文) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.15 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/8.7 kg | 15 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.6~0.7 % | ASTM D 955 | |
横向(Across Flow) | 0.5~0.9 % | ASTM D 955 | |
磨耗 | 80 mg/1000cy | ASTM D 1044 | 1000g,H-22 wheel |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 44.1 Mpa | ASTM D 412 | |
50%延伸率时 | 13.4 Mpa | ASTM D 412 | |
100%延伸率时 | 16.5 Mpa | ASTM D 412 | |
300%延伸率时 | 31.7 Mpa | ASTM D 412 | |
拉伸延伸率 | |||
断裂(brk) | 425 % | ASTM D 412 | |
弯曲模量 | 172 Mpa | ASTM D790 | |
撕裂强度 | 158 N/mm | ASTM D 624 | Die C |
压缩永久形变 | 25 % | ASTM D 395 | Method B, 22 hrs @ 25° C |
压缩永久形变 | 30 % | ASTM D 395 | Method B, 22 hrs @ 70° C |
拉伸断后形变 | 30 % | ASTM D 412 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 96 A | ASTM D 2240 | |
邵氏硬度 D | 55 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 104 °C | ASTM D1525 | 120° C/hr, 9.8N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 130 E-6 cm/cm/℃ | ASTM D 696 |