IROGRAN® A 70 E 4675
TPU(热塑性聚氨酯)
亨斯迈(Huntsman)
产品描述
IROGRAN A 70 E 4675 is a softener free thermoplastic special-polyester-polyurethane for injection moulding applications.
Additional characteristics of the product are very short cycle times and high dimensional stability.
PERFORMANCE FEATURES
Easy demolding
High demolding stability
Short cycle times
Softener-free
High elasticity
APPLICATIONS
For the production of casual shoe soles, cable bushings, plugs, buffers.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 尺寸稳定短周期成型易脱模 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.15 g/cm³ | ISO 1183 | |
密度 | 1.15 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
190℃/21.6 kg | 30 cm³/10 min | Internal | |
收缩率 | |||
- | 2.5 % | Internal | |
磨耗 | 80 mm³ | ISO 4649 | |
磨耗 | 91.8 mm³ | ISO 4649 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
100%延伸率时 | 3.93 Mpa | ASTM D 412 | |
100%延伸率时 | 3.3 Mpa | DIN 53504 | |
300%延伸率时 | 6.55 Mpa | ASTM D 412 | |
300%延伸率时 | 5.8 Mpa | DIN 53504 | |
- | 15.2 Mpa | ASTM D 412 | |
- | 30 Mpa | DIN 53504 | |
拉伸延伸率 | |||
断裂(brk) | 650 % | ASTM D 412 | |
断裂(brk) | 650 % | DIN 53504 | |
撕裂强度 | 45 N/mm | ISO 34 | |
撕裂强度 | 52.5 N/mm | ASTM D 624 | |
压缩永久形变 | 35 % | ASTM D 395 | 24 hrs@23℃ |
压缩永久形变 | 45 % | ASTM D 395 | 24 hrs@70℃ |
压缩永久形变 | 35 % | ISO 815 | 24 hrs@23℃ |
压缩永久形变 | 58 % | ISO 815 | 24 hrs@70℃ |
回弹性 | 25 % | Internal | Bayshore Rebound Resilience |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 75 A | ASTM D 2240 | |
邵氏硬度 A | 75 A | ISO 868 | |
邵氏硬度 D | 25 D | ISO 868 | |
邵氏硬度 D | 25 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 125~190 °C | Internal |