IROGRAN® A 92 P 4851
TPU(热塑性聚氨酯)
亨斯迈(Huntsman)
产品描述
IROGRAN A 92 P 4851 is a thermoplastic polyether-polyurethane for injection moulding and extrusion applications.
Additional characteristics of the product are high extrudability and low-adhesion surfaces.
PERFORMANCE FEATURES
Excellent hydrolysis resistance
High microbial resistance
High stability of melt
High production rates
Low-adhesion surfaces
APPLICATIONS
For the production of jacket material for cables, jackets for high pressure spiral hoses, profiles.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗菌防微生物耐水解 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
密度 | 1.14 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
190℃/21.6 kg | 55 cm³/10 min | Internal | |
收缩率 | |||
- | 0.5 % | Internal | |
磨耗 | 16.4 mm³ | ISO 4649 | |
磨耗 | 35 mm³ | ISO 4649 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
100%延伸率时 | 1450 psi | ASTM D 412 | |
100%延伸率时 | 10 Mpa | DIN 53504 | |
300%延伸率时 | 2100 psi | ASTM D 412 | |
300%延伸率时 | 16 Mpa | DIN 53504 | |
- | 5200 psi | ASTM D 412 | |
- | 40 Mpa | DIN 53504 | |
拉伸延伸率 | |||
断裂(brk) | 630 % | ASTM D 412 | |
断裂(brk) | 600 % | DIN 53504 | |
撕裂强度 | 75 N/mm | ISO 34 | |
撕裂强度 | 112.1 N/mm | ASTM D 624 | |
压缩永久形变 | 25 % | ASTM D 395 | 24 hrs@23℃ |
压缩永久形变 | 45 % | ASTM D 395 | 24 hrs@70℃ |
压缩永久形变 | 25 % | ISO 815 | 24 hrs@23℃ |
压缩永久形变 | 45 % | ISO 815 | 24 hrs@70℃ |
回弹性 | 33 % | Internal | Bayshore Rebound Resilience |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 93 A | ASTM D 2240 | |
邵氏硬度 A | 93 A | ISO 868 | |
邵氏硬度 D | 42 D | ISO 868 | |
邵氏硬度 D | 42 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 160~171 °C | Internal |