Texin® 260
TPU(热塑性聚氨酯)
科思创 (原拜耳)(Covestro)
产品描述
Texin 260 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 60D. It can be processed by injection molding; extrusion processes are not recommended.
Texin 260 resin offers outstanding abrasion resistance, impact strength, toughness, and flexibility. It also exhibits excellent fuel and oil resistance. Texin 260 natural color resin complies with FDA food-contact regulations 21 CFR 177.1680 (Polyurethane Resins) and 177.2600 (Rubber Articles Intended for Repeated Use), subject to the limitations of these and any other applicable regulations. Typical applications include toplifts, casters, grommets, and seals. As with any product, use of Texin 260 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击高韧性耐磨食品接触级耐燃油耐油 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.22 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.8 % | ASTM D 955 | 2.54 mm |
横向(Across Flow) | 0.8 % | ASTM D 955 | 2.54 mm |
磨耗 | 50 mg/1000cy | ASTM D 3489 | H-18, 1,000-g Load |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
50%延伸率时 | 20 Mpa | ASTM D 412 | |
100%延伸率时 | 22.1 Mpa | ASTM D 412 | |
300%延伸率时 | 40 Mpa | ASTM D 412 | |
- | 60 Mpa | ASTM D 412 | |
拉伸延伸率 | |||
断裂(brk) | 420 % | ASTM D 412 | |
弯曲模量 | 296 Mpa | ASTM D790 | 73°F (23°C) |
撕裂强度 | 175 kN/m | ASTM D 624 | Die C |
压缩永久形变 | 55 % | ASTM D 395 | 22 Hours at 158°F (70°C) |
压缩永久形变 | 27 % | ASTM D 395 | 22 Hours at 73°F (23°C) |
压缩永久形变 | 35 % | ASTM D 395 | Postcured, 22 Hours at 158°F (70°C) |
压缩永久形变 | 21 % | ASTM D 395 | Postcured, 22 Hours at 73°F (23°C) |
抗压强度 | 9.4 Mpa | ASTM D 575 | 10% Deflection |
抗压强度 | 13.4 Mpa | ASTM D 575 | 15% Deflection |
抗压强度 | 0.34 Mpa | ASTM D 575 | 2% Deflection |
抗压强度 | 17.4 Mpa | ASTM D 575 | 20% Deflection |
抗压强度 | 21.7 Mpa | ASTM D 575 | 25% Deflection |
抗压强度 | 3.6 Mpa | ASTM D 575 | 5% Deflection |
抗压强度 | 53.7 Mpa | ASTM D 575 | 50% Deflection |
回弹性 | 35 % | ASTM D 2632 | Bayshore Resilience |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -68 °C | ASTM D 746 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 60 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 60 °C | ASTM D648 | |
维卡软化温度(Vicat) | 190 °C | ASTM D1525 | Rate A |
线性膨胀系数(CLTE) | |||
- | 126 E-6 mm/mm/℃ | ASTM D 696 | |
玻璃化温度(Tg) | -15 °C | Internal |