PRE-ELEC® TP 16159
TPU(热塑性聚氨酯)
普宓斯(PREMIX)
产品描述
PRE-ELEC® TP 16159 is a conductive thermoplastic elastomer compound based on a polyester thermoplastic polyurethane (TPU). Conductivity is achieved by using special conductive carbon fibre. In addition to a low electrical resistivity, it has excellent mechanical properties due to carbon fibre reinforcement. The grade is suitable for extrusion and injection moulding applications.
基本信息
| 原厂资料 | 物性表(英文) PRE-ELEC牌号选择 | |||
| 产品特性 | 导电 | |||
| 成型方式 | 注塑挤出 | |||
| 增强填充 | 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.28 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/10 kg | 33 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.1 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 50 Mpa | ISO 527 | |
拉伸延伸率 | |||
断裂(brk) | 25 % | ISO 527 | |
弯曲模量 | 660 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 71 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 62 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 87 °C | ISO 75/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 55 °C | ISO 75/Af | |
维卡软化温度(Vicat) | 62 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 120 °C | ISO 306/A50 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 9E+0 Ohm-cm | Internal | |
表面电阻率 | 2E+4 Ohm | IEC 61340-2-3 |