Addigy® PPU 86AW6 000000 F EXFW
TPU(热塑性聚氨酯)
科思创 (原拜耳)(Covestro)
产品描述
Additive manufacturing thermoplastic polyurethane grade for powder bed fusion such as Selective Laser Sintering (SLS) and High Speed Sintering (HSS).
Extra-high powder flowability, useful for e.g. roller or blade coating systems. Aliphatic ether/ester type; good low-temperature flexibility; high rebound resilience; microbial and hydrolysis resistance; no yellowing under the action of UV light.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗菌防微生物抗紫外线耐水解 | |||
| 颜色形状 | 粉末状本色 | |||
| 成型方式 | 激光烧结(SLS)3D打印 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.46 g/cm³ | Internal | powder bed |
密度 | 1.02 g/cm³ | Internal | printed bar |
吸水率 | 1 % | ISO 15512 | |
粒子大小 | 35 micrometer | Internal | X10 |
粒子大小 | 80 micrometer | Internal | X50 |
粒子大小 | 125 micrometer | Internal | X90 |
堆积(视)密度 | 0.42 g/cm³ | Internal | powder |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 9 Mpa | DIN 53504 | xy-direction, 200 mm/min |
- | 4 Mpa | DIN 53504 | z-direction, 200 mm/min |
拉伸延伸率 | |||
断裂(brk) | 416 % | DIN 53504 | xy-direction, 200 mm/min |
断裂(brk) | 62 % | DIN 53504 | z-direction, 200 mm/min |
撕裂强度 | 96 kN/m | ISO 34 | xy-direction |
撕裂强度 | 30 kN/m | ISO 34 | z-direction |
回弹性 | 68 % | DIN 53512 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 85~89 A | ISO 7619-1 | 1s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 100~150 °C | Internal | DMA (1 Hz; 2 °C/min) |
玻璃化温度(Tg) | -48 °C | ISO 6721 | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
粉末压缩性指数(豪斯纳比) | 1.35 - | ISO 787-11 |