IROGRAN® A 85 E 4719
TPU(热塑性聚氨酯)
亨斯迈(Huntsman)
产品描述
IROGRAN A 85 E 4719 is a thermoplastic polyester polyurethane for melt calendering.
IROGRAN is part of the HUNTSMAN technical extrusion and injection molding product range and offers a specially designed, flexible material with a broad processing window.
PERFORMANCE FEATURES
High wear resistance
Good melt flow
High elasticity
Complies with FDA CFR 175.105 / 177.2600
APPLICATIONS
Texile Coatings
Technical molding
Cable jacketing
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨良好流动性 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 成型方式 | 压延注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.21 g/cm³ | ASTM D792 | |
密度 | 1.21 g/cm³ | DIN 53479 | |
熔体体积流动速率(MVR) | |||
190°C/10.0 kg | 60 cm³/10 min | ISO 1133 | |
磨耗 | 19.7 mm³ | Internal | |
磨耗 | 20 mm³ | DIN 53516 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
100%延伸率时 | 6.7 Mpa | ASTM D 412 | |
100%延伸率时 | 6 Mpa | DIN 53504 | |
300%延伸率时 | 11.7 Mpa | ASTM D 412 | |
300%延伸率时 | 11.7 Mpa | DIN 53504 | |
- | 28.3 Mpa | ASTM D 412 | |
- | 35 Mpa | DIN 53504 | |
拉伸延伸率 | |||
断裂(brk) | 600 % | ASTM D 412 | |
断裂(brk) | 620 % | DIN 53504 | |
撕裂强度 | 99.8 N/mm | ASTM D 624 | |
撕裂强度 | 80 N/mm | DIN 53515 | |
压缩永久形变 | 30 % | ASTM D 395 | 24 hrs@23℃ |
压缩永久形变 | 42 % | ASTM D 395 | 24 hrs@70℃ |
压缩永久形变 | 30 % | DIN 53517 | 24 hrs@23℃ |
压缩永久形变 | 42 % | DIN 53517 | 24 hrs@70℃ |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 85 A | ASTM D 2240 | |
邵氏硬度 A | 85 A | DIN 53505 | |
邵氏硬度 D | 36 D | ASTM D 2240 | |
邵氏硬度 D | 36 D | DIN 53505 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热机械分析(TMA) | 160 °C | Internal | TMA High |
热机械分析(TMA) | 115 °C | Internal | TMA Low |