Hifax TYC 762P
TPO(POE聚烯烃弹性体)
利安德巴塞尔(LyondellBasell)
产品描述
This information has been secured during the course of product development. Both the product and its properties are subject to change before final commercialization.
Hifax TYC 762P very high melt flow, 1,600 MPa flexural modulus, precolored, UV-stabilized, mineral-filled, paintable thermoplastic elastomeric olefin has an excellent balance of properties, processability, and paintability. It was designed primarily for automotive bumper fascias.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性良好冲击性尺寸稳定易成型易涂装易脱模抗紫外线高流动填充增强 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.03 g/cm3 | ISO 1183 | Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 28 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 17 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 13 % | ISO 527-1/-2 | |
弯曲模量 | 1600 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 4 kJ/m2 | ISO 180 | |
23℃ (73℉) | 30 kJ/m2 | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 94 °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） | 56 °C | ISO 75-1/-2 | Unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 40 E-6 cm/cm/℃ | ISO 11359-1/-2 | -30°C to 100°C |