Sequel 2420
TPO(POE聚烯烃弹性体)
利安德巴塞尔(LyondellBasell)
产品描述
Sequel 2420 high melt flow, very high flexural modulus, mineral-filled thermoplastic elastomeric olefin has an excellent balance of properties. It was designed primarily for applications that require stiffness, dimensional stability, high impact characteristics and improved surface durability. This material can be used for applications where other engineering polymers have been used, such as ABS, PC/ABS, or PC/PBT blends.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性高冲击良好表面耐刮擦尺寸稳定易成型填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.04 g/cm3 | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 20 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 26 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 100 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
弯曲模量 | 2300 Mpa | ISO 178 | 23 °C, 2 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 4 kJ/m2 | ISO 180 | |
23℃ (73℉) | 15 kJ/m2 | ISO 180 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 65 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 120 °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） | 60 °C | ISO 75-1/-2 | Unannealed |