Hifax RTA3263EUV
TPO(POE聚烯烃弹性体)
利安德巴塞尔(LyondellBasell)
产品描述
"Hifax" RTA3263EUV fractional melt flow, 1,500 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent combination of rigidity, impact resistance, melt strength, processability and weatherability. It was designed specifically for thermoformed applications.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高刚性良好冲击性易成型抗紫外线耐候性高粘度高熔体强度填充增强 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 挤出片材挤出型材挤出管材挤出 | |||
| 增强填充 | 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.1 g/cm3 | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 0.8 g/10min | ASTM D 1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 19 Mpa | ASTM D638 | |
断裂(brk) | 21 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 400 % | ASTM D638 | |
断裂(brk) | 450 % | ASTM D638 | |
弯曲模量 | 1200 Mpa | ASTM D790 | |
弯曲模量 | 1500 Mpa | ASTM D790 | |
撕裂强度 | 110 kN/m | ASTM D 624 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 750 J/m | ASTM D256 | |
落锤冲击 | 32 J | ASTM D 5420 | Gardner Impact |
脆化温度 | -30 °C | ASTM D 746 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 65 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 74 °C | ASTM D648 | Unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 41 E-6 cm/cm/℃ | ASTM D 696 |