Hifax X 1956 A
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Hifax X 1956 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell`s proprietary Catalloy process technology. This grade is primarily used in polyolefin-based compounds to improve mechanical properties and enhance moulded part appearance. In particular, the product is used by our customers for providing tiger stripe resistance and improved aesthetics for unpainted automotive components. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高强度良好冲击性良好柔韧性颜色稳定/易着色高粘度 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 压延注塑挤出热成型共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.89 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 0.9 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527-1/-2 | |
断裂(brk) | 30 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 12 % | ISO 527-1/-2 | |
断裂(brk) | 500 % | ISO 527-1/-2 | |
弯曲模量 | 800 Mpa | ISO 178 | |
撕裂强度 | 67 kN/m | ASTM D 624 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 5 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 10 kJ/m2 | ISO 179 | Complete Break |
23℃ (73℉) | 95 kJ/m2 | ISO 179 | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 57 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 70 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 145 °C | ISO 306/A50 | |
熔融温度(Tm) | 163 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
光泽度 | 57 - | ASTM D 2457 | 60°, 45 mil |