Hifax 7430 XEP
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Hifax 7430 XEP is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is a high melt flow, medium-high flexural modulus, highly crystalline copolymer with good balance of impact and stiffness. It is primarily used in interior trim applications requiring low temperature high speed impact performance. It is also used as a component in compounded materials for automotive and industrial applications. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性耐低温冲击高流动共聚物 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.89 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 18.5 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527-1/-2 | |
断裂(brk) | 14 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-1/-2 | |
断裂(brk) | 32 % | ISO 527-1/-2 | |
弯曲模量 | 1200 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 2.8 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 6.7 kJ/m2 | ISO 179 | Complete Break |
23℃ (73℉) | 14 kJ/m2 | ISO 179 | Complete Break |
多轴冲击 | 18 J | ASTM D3763 | -40°C, 3.20 mm, Ductile Failure |
多轴冲击 | 28 J | ASTM D3763 | 23°C, 3.20 mm, Ductile Failure |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 55 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 82 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 131 °C | ISO 306/A50 | |
熔融温度(Tm) | 163 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
光泽度 | 49 - | ASTM D 2457 | 60°, 45 mil |
原材料现货供应: