Adflex KS 311 P
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Adflex KS 311 P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for extrusion as well as injection molding and blow molding applications, including mechanical and decorative automotive parts requiring elastomeric type properties, like molded-in color automotive exterior components. The product is used by our customers for applications with paintable and weatherable requirements, such as injection molded fascias, claddings, bumper covers, body panels, step pads, and air deflectors. It is also used as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击良好表面颜色稳定/易着色易成型易脱模 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 流延薄膜注塑吹塑共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.89 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 9.5 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 14 Mpa | ISO 527-1/-2 | |
断裂(brk) | 15 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 14 % | ISO 527-1/-2 | |
断裂(brk) | 800 % | ISO 527-1/-2 | |
弯曲模量 | 530 Mpa | ISO 178 | |
撕裂强度 | 103 kN/m | ASTM D 624 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 1.4 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 4.1 kJ/m2 | ISO 179 | Partial Break |
23℃ (73℉) | 59 kJ/m2 | ISO 179 | Partial Break |
多轴冲击 | 26 J | ASTM D3763 | -40°C, 3.20 mm, Ductile Failure |
多轴冲击 | 14 J | ASTM D3763 | 23°C, 3.20 mm, Ductile Failure |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 46 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 53 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 112 °C | ISO 306/A50 | |
熔融温度(Tm) | 142 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 82 % | ASTM D1003 | 1140 μm |
光泽度 | 76 - | ASTM D 2457 | 60°, 1140 μm |