Adflex X 101 H
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Adflex X 101 H is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell'
s proprietary Catalloy process technology . It exhibits a high softness and a low modulus, with a relatively high melt flow index. Adflex X 101 H is tailored to replace atactic polypropylene copolymers (APP) used for the modification of bitumen in roofing membranes. The percentage to be added can vary according to the quantity of the atactic polypropylene used in combination with Adflex X 101 H and the requested cold bending temperature of the end product. Due to the high molecular weight of Adflex X 101 H, high blend viscosity and good penetration values
are obtained. Its structure is tailored to obtain easy dispersion and phase inversion in the bitumen blend. Adflex X101H is also used in other industrial applications where high flexibility and the capability of accepting high filler loading levels are required. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击ESCR耐化学性高流动软质 | |||
| 成型方式 | 流延薄膜注塑共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.88 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 8 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6 Mpa | ISO 527-1/-2 | |
断裂(brk) | 10 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 40 % | ISO 527-1/-2 | |
断裂(brk) | 600 % | ISO 527-1/-2 | |
弯曲模量 | 80 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 3.6 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 105 kJ/m2 | ISO 179 | Partial Break |
23℃ (73℉) | 40 kJ/m2 | ISO 179 | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 30 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 39 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 54 °C | ISO 306/A50 | |
熔融温度(Tm) | 142 °C | ISO 11357-3 | DSC |