Adflex V 109 F
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Adflex V 109 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell'
s proprietary Catalloy process technology. It is primarily used for molding, impact modification, extrusion coating and film applications. This resin can be used on conventional injection molding or extrusion equipment. Adflex V 109 F features a very high softness and low modulus, with a relatively high melt flow. The grade is available in natural pellet form.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击软质 | |||
| 成型方式 | 流延薄膜注塑共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.88 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 12 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 5 Mpa | ISO 527-1/-2 | |
断裂(brk) | 8 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 40 % | ISO 527-1/-2 | |
断裂(brk) | 800 % | ISO 527-1/-2 | |
弯曲模量 | 80 Mpa | ISO 178 | |
撕裂强度 | 65 kN/m | ASTM D 624 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 1.4 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 5 kJ/m2 | ISO 179 | Partial Break |
23℃ (73℉) | 35 kJ/m2 | ISO 179 | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 30 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 35 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 55 °C | ISO 306/A50 | |
熔融温度(Tm) | 142 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 49 % | ASTM D1003 | 1140 μm |
光泽度 | 62 - | ASTM D 2457 | 60°, 1140 μm |