Adflex Q 108 F
TPO(热塑性聚烯烃)
利安德巴塞尔(LyondellBasell)
产品描述
Adflex Q 108 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene and other compounding applications, as well as monolayer and multilayer air quenched blown films. It is also used by our customers for automotive color-matched interior trim applications. The grade is available in natural pellet form and has no slip or antiblock, and only minimal stabilization in order to allow wider design latitude for the compounder. Additional suitable stabilization is recommended to protect the resin during melt processing and throughout its useful life.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击低光泽颜色稳定/易着色ESCR | |||
| 成型方式 | 挤出吹塑热成型 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.88 g/cm3 | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 0.6 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 10 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
断裂(brk) | 500 % | ISO 527-1/-2 | |
弯曲模量 | 100 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 2.8 kJ/m2 | ISO 179 | Complete Break |
-20℃ (-4℉) | 107 kJ/m2 | ISO 179 | Partial Break |
23℃ (73℉) | 41 kJ/m2 | ISO 179 | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 30 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 40 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 60 °C | ISO 306/A50 | |
熔融温度(Tm) | 142 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 47 % | ASTM D1003 | 1140 μm |
雾度 | 9 % | ASTM D1003 | 50.0 μm |
光泽度 | 87 - | ASTM D 2457 | 45°, 50.0 μm |
光泽度 | 50 - | ASTM D 2457 | 60°, 1140 μm |