OnFlex™ HT thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds is specially formulated to deliver very good compression set performance at elevated temperatures and a high heat resistance. Furthermore, OnFlex™ HT compounds offer excellent mechanical properties, a wide hardness range and good processability.
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1 g/cm³
| ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
11 Mpa | DIN 53504 | Across Flow, 23°C, 2.00 mm, 200 mm/min |
断裂(brk) |
9 Mpa | DIN 53504 | Flow, 23°C, 2.00 mm, 200 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
750 % | DIN 53504 | Across Flow, 23°C, 2.00 mm, 200 mm/min |
断裂(brk) |
650 % | DIN 53504 | Flow, 23°C, 2.00 mm, 200 mm/min |
压缩永久形变 | 44 %
| ISO 815 | -10°C, 22 hr |
压缩永久形变 | 53 %
| ISO 815 | 100°C, 22 hr |
压缩永久形变 | 27 %
| ISO 815 | 23°C, 72 hr |
压缩永久形变 | 44 %
| ISO 815 | 70°C, 22 hr |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 80 A
| DIN 53505 | 3 sec, 23°C, 6.00 mm, Injection Molded |