OnFlex™ HT 50A-3S2099
TPE(TPR)
埃万特(原普立万)(Avient)
产品描述
OnFlex™ HT thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds is specially formulated to deliver very good compression set performance at elevated temperatures and a high heat resistance. Furthermore, OnFlex™ S HT compounds are in compliance with EN 681-2 and offer excellent mechanical properties, a wide hardness range and good processability.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 耐热易成型耐臭氧 | |||
法规认证 | EN 681(弹性体密封件)RoHS(欧盟电子电气设备中有害物质) | |||
颜色形状 | 粒状 | |||
成型方式 | 注塑挤出 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1 g/cm³ | ISO 1183 | |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 9.4 Mpa | DIN 53504 | Across Flow, 23°C, 2.00 mm, 200 mm/min |
断裂(brk) | 5.2 Mpa | DIN 53504 | Flow, 23°C, 2.00 mm, 200 mm/min |
100%延伸率时 | 1.1 Mpa | ISO 37 | Across Flow |
100%延伸率时 | 1.7 Mpa | ISO 37 | Flow |
300%延伸率时 | 1.9 Mpa | ISO 37 | Across Flow |
300%延伸率时 | 2.9 Mpa | ISO 37 | Flow |
拉伸延伸率 | |||
断裂(brk) | 800 % | DIN 53504 | Across Flow, 23°C, 2.00 mm, 200 mm/min |
断裂(brk) | 560 % | DIN 53504 | Flow, 23°C, 2.00 mm, 200 mm/min |
撕裂强度 | 27 kN/m | ISO 34 | |
压缩永久形变 | 36 % | ISO 815 | -10°C, 22 hr |
压缩永久形变 | 50 % | ISO 815 | -10°C, 72 hr |
压缩永久形变 | 42 % | ISO 815 | 100°C, 22 hr |
压缩永久形变 | 46 % | ISO 815 | 125°C, 22 hr |
压缩永久形变 | 69 % | ISO 815 | 150°C, 22 hr |
压缩永久形变 | 20 % | ISO 815 | 23°C, 72 hr |
压缩永久形变 | 27 % | ISO 815 | 70°C, 22 hr |
应力松弛 | 24 % | ISO 3384 | 100d, 25% compression, Method A |
应力松弛 | 13 % | ISO 3384 | 168hrs, 25% compression, Method A |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 50 A | DIN 53505 | 3 sec, 23°C, 6.00 mm, Injection Molded |
橡胶硬度IRHD | 60 - | ISO 48 | |
老化性能 | 值/单位 | 测试标准 | 测试条件 |
硬度 (热老化) | 3 % | DIN 53505 | in Air (Shore A, 70°C, 168 hr) |
拉伸强度(热老化) | -3 % | DIN 53504 | in Air (70°C, 168 hr, 2.00 mm) |
延伸率(热老化) | 3 % | DIN 53504 | at Break in Air (70°C, 168 hr, 2.00 mm) |
体积变化 | -0.6 % | ISO 1817 | 70°C, 168 hr, in Water |
体积变化 | 16 % | ISO 1817 | 70°C, 72 hr, in ASTM #1 Oil |