Dow ENDURANCE™ HFDA-0800 BK EC
TP热塑性塑料
陶氏化学(Dow Chemical)
产品描述
DOW ENDURANCE™ HFDA-0800 BK EC is a specially formulated semiconductive, vulcanizable compound designed for conductor shield and bonded insulation shield applications in medium and high voltage crosslinked polyethylene insulated cables.(1) DOW ENDURANCE™ HFDA-0800 BK EC has stable volume resistivity characteristics at elevated temperatures and is formulated with a polymer system that has demonstrated compatibility with copper conductor.
DOW ENDURANCE™ HFDA-0800 BK EC was specifically developed utilizing a special acetylene carbon black to provide a supersmooth surface to achieve best in class performance and yielding a more perfect interface between the extruded shield and the insulation. As a result, significantly improved cable performance can be expected.
Specifications
DOW ENDURANCE™ HFDA-0800 BK EC is designed for use in power distribution cables. Cables with conductor and insulation shielding of DOW ENDURANCE™ HFDA-0800 BK EC, prepared using sound commercial fabrication practice, would be expected to meet the following specifications:
ANSI/ICEA: S-94-649, S-97-682, S-93-639 / NEMA WC74
AEIC: CS8
IEC: 60502
(1) DOW ENDURANCE™ MV A-0800 is recommended for use in conjunction with DOW cross-linked polyethylene and tree-retardant cross-linked polyethylene compounds. For other polymer insulations such as EPR and EPDM's the user is cautioned to establish the utility of DOW ENDURANCE™ MV A-0800 with each formulation.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 半导体可交联 | |||
颜色形状 | 黑色 | |||
成型方式 | 线缆挤出 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.15 g/cm³ | ASTM D792 | |
环境应力开裂(ESCR ) | 504 Hours | ASTM D 1693 | 100% Igepal, F0 |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 14.5 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
断裂(brk) | 200 % | ASTM D638 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -40 °C | ASTM D 746 | |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 6.5E+1 Ohm-cm | ASTM D 991 | 130°C |
体积电阻率 | 1.5E+1 Ohm-cm | ASTM D 991 | 23°C |
体积电阻率 | 6E+1 Ohm-cm | ASTM D 991 | 90°C |