Fortron® ICE 504L
PPS(聚苯硫醚)
塞拉尼斯(Celanese)
产品描述
40% Glass-filled, improved crystallization
FORTRON ICE 504L is a 40% glass fiber reinforced polyphenylene sulfide, that belongs to our new generation of Fortron® PPS.
This new technology allows optimization of molding conditions with faster cycle times. Due to the faster crystallization of the material at a higher temperature, the option of mold wall temperature reduction can be subject of advanced process optimization. The potential for optimization of Fortron® ICE by cycle time reduction is possible by standard cavity surface temperatures of 140°C. The potential for lowering the mold temperature must be checked individually and it depends on process and part design.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 短周期成型填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 40% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.65 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4, 2577 | |
横向(Across Flow) | 0.6 % | ISO 294-4, 2577 | |
吸水率 | 0.02 % | ISO 62 | 23°C-sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 202 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 1.9 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
断裂(brk) | 294 Mpa | ISO 178 | |
弯曲模量 | 15000 Mpa | ISO 178 | 23°C |
拉伸模量 | 15100 Mpa | ISO 527-2/1A | |
压缩模量 | 15000 Mpa | ISO 604 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 53 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 53 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 34 kJ/m² | ISO 180/1U | |
23℃ (73℉) | 34 kJ/m² | ISO 180/1U | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 100 M | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 270 °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | 215 °C | ISO 75-1/-2 | |
比热容 | 1500 J/kg-K | - | Melt |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 26 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 42 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 280 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | 90 °C | ISO 11357-1/-2 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.38 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
氧指数(LOI) | 47 % | ISO 4589-1/-2 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
2mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 825 °C | IEC 60695-2-13 | |
2.0mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
介电常数(DK) | |||
1MHz | 4.1 - | IEC 60250 | |
耗散因数(DF) | |||
1MHz | 20 E-4 | IEC 60250 | |
绝缘强度 | 28 kV/mm | IEC 60243-1 |