Fortron® 1115L0
PPS(聚苯硫醚)
塞拉尼斯(Celanese)
产品描述
Fiberglass reinforced with high melt strength for blow molding & extrusion applications
Fortron® 1115L0 is a 15% fiberglass-reinforced grade of polyphenylene sulfide with high melt strength suitable for blow molding and extrusion applications. The recommended processing conditions are similar to those of our standard grades, except drying conditions are somewhat milder at 80 to 100 C for 3-4 hours.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃高熔体强度填充增强 | |||
| 成型方式 | 挤出吹塑 | |||
| 增强填充 | 15% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.44 g/cm³ | ISO 1183 | |
吸水率 | 0.02 % | ISO 62 | 23°C-sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 120 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
- | 200 Mpa | ISO 178 | 23°C |
弯曲模量 | 7500 Mpa | ISO 178 | 23°C |
拉伸模量 | 7700 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 32 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.2 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 220 °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | 115 °C | ISO 75-1/-2 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.75 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 |