Fortron® 1140L7
PPS(聚苯硫醚)
塞拉尼斯(Celanese)
产品描述
One of the easiest flowing 40% glass reinforced grade in the Fortron product line. This material can be processed at fast cycle times due to the unique crystallization characteristics. This product offers good heat and chemical resistance, as well as, good electrical properties. The product is inherently flame-retardant and exhibits high hardness and rigidity.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热阻燃短周期成型耐化学性高流动填充增强 | |||
| 增强填充 | 40% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.65 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4, 2577 | |
横向(Across Flow) | 0.5~0.7 % | ISO 294-4, 2577 | |
吸水率 | 0.02 % | ISO 62 | 23°C-sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 170 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 1.6 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
断裂(brk) | 260 Mpa | ISO 178 | |
弯曲模量 | 14500 Mpa | ISO 178 | 23°C |
拉伸模量 | 14500 Mpa | ISO 527-2/1A | |
压缩模量 | 14000 Mpa | ISO 604 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 8 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 100 M | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 270 °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | 200 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 280 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | 90 °C | ISO 11357-1/-2 | 10°C/min |
加工温度 | 310~340 °C | - | Injection |
模具温度 | 135~160 °C | - | Injection |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.38 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
相比漏电起痕指数(CTI ) | |||
- | 125 - | IEC 60112 | |
绝缘强度 | 26 kV/mm | IEC 60243-1 |