DIC® FZ-928N Black
PPS(聚苯硫醚)
迪爱生 (DIC)
产品描述
■ Out line: FZ-928N Black is glass fiber reinforced PPS compound which is developed to provide a excellent adhesive bonding, toughness, and thin wall flow ability. ■ Color: Black
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性良好粘合性高流动填充增强 | |||
| 颜色形状 | 黑色 | |||
| 增强填充 | 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.42 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.32 % | ASTM D 955 | |
横向(Across Flow) | 1.2 % | ASTM D 955 | |
吸水率 | 0.02 % | ASTM D570 | 23℃,24Hrs. /in water |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 135 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
断裂(brk) | 2.1 % | ASTM D638 | |
弯曲强度 | |||
- | 180 Mpa | ASTM D790 | |
弯曲应变 | |||
断裂(brk) | 3.4 % | ASTM D 790 | |
弯曲模量 | 6600 Mpa | ASTM D790 | |
拉伸模量 | 7500 Mpa | ASTM D638 | |
泊松比 | 0.37 - | - | |
摩擦系数 | 0.35 - | Internal | dynamic,P=150KPa, V=0.3m/s, PPS vs. carbon steel |
摩擦系数 | 0.35 - | Internal | static,P=150KPa, V=0.3m/s, PPS vs. carbon steel |
抗压强度 | 170 Mpa | ASTM D 695 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 100 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 650 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 84 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 230 °C | ASTM D648 | |
线性膨胀系数(CLTE) | |||
- | 35 E-6/K | ASTM D 696 | -30 to 90℃ |
加工温度 | 290~320 °C | - | |
模具温度 | 120~150 °C | - | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
1MHz | 4 - | ASTM D 150 | |
耗散因数(DF) | |||
1MHz | 20 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
- | 180 V | ASTM D 3638 | |
绝缘强度 | 24 kV/mm | ASTM D149 | t=1.6mm |
耐电弧性 | 120 sec | ASTM D495 |