LNP™ LUBRICOMP™ OCP36
PPS(聚苯硫醚)
沙特基础 (SABIC)
产品描述
LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electrically Conductive.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电耐磨填充增强 | |||
| 增强填充 | 30% 碳纤15% PTFE+硅 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.51 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.2 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.4~0.6 % | ASTM D 955 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 166 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 166 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 253 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 1.6 % | ASTM D638 | |
断裂(brk) | 0.9 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 254 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 254 Mpa | ISO 178 | 2 mm/min |
- | 253 Mpa | ASTM D790 | |
弯曲应变 | |||
断裂(brk) | 1.4 % | ISO 178 | 2 mm/min |
弯曲模量 | 21400 Mpa | ASTM D790 | |
弯曲模量 | 22240 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 26120 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 24890 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.47 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.33 - | ASTM D 3702 | Static COF |
磨损因数 | 24 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 53 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 485 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 260 °C | ASTM D648 | 3.2 mm, unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2 Ohm | ASTM D257 |