Fortron® 1140L0 FC
PPS(聚苯硫醚)
塞拉尼斯(Celanese)
产品描述
Fortron 1140L0 FC is a 40% glass-reinforced extrusion grade for food contact applications. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. 1140L0 is used to produce rods and slabs.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热阻燃易焊接食品接触级耐化学性填充增强 | |||
| 成型方式 | 挤出片材挤出型材挤出 | |||
| 增强填充 | 40% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.65 g/cm³ | ISO 1183 | |
吸水率 | 0.02 % | ISO 62 | 23°C-sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 185 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 1.9 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
断裂(brk) | 280 Mpa | ISO 178 | |
弯曲模量 | 14000 Mpa | ISO 178 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 280 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | 90 °C | ISO 11357-1/-2 | 10°C/min |
加工温度 | 310~340 °C | - | Injection |
模具温度 | 135~160 °C | - | Injection |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.38 mm | UL94 | |
V-0 | 1.5 mm | UL94 |