Therma-Tech™ TT9200-5001 EI White
Therma-Tech™ TT9200-5001 EI White
PPS(聚苯硫醚)
埃万特(原普立万)(Avient)
产品描述
Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 导热阻燃无卤绝缘填充增强 |
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) |
| 颜色形状 | 粒状白色 |
| 成型方式 | 注塑挤出 |
| 增强填充 | 玻纤 矿物 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 2.91 g/cm³
| ISO 1183 | |
收缩率 | | | |
纵向(Flow) |
0.1~0.4 % | ISO 294-4 | Injection Molded |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
75 Mpa | ISO 527 | |
拉伸延伸率 | | | |
断裂(brk) |
0.5~1 % | ISO 527 | Type I, 50 mm/min |
弯曲强度 | | | |
- |
90 Mpa | ISO 178 | 10 mm/min, Injection Molded |
弯曲模量 | 12300 Mpa
| ISO 178 | 10 mm/min, Injection Molded |
拉伸模量 | 15000 Mpa
| ISO 527 | Type I, 1.0 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
3.5 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
12 kJ/m² | ISO 179 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
220 °C | ISO 75-2/A | Annealed |
导热系数 | 0.8~1.2 W/(m K)
| ASTM E 1461 | 23°C, In Plane |
导热系数 | 0.7~1.1 W/(m K)
| ASTM E 1461 | 23°C, Through Plane |
加工温度 | 310~340 °C
| - | Injection |
模具温度 | 140~170 °C
| - | Injection |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-0 |
1.6 mm | UL94 | |
灼热丝可燃性指数(GWFI) | | | |
3mm |
960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1.0E+11 Ohm
| IEC 60093 | |
绝缘强度 | 4 kV/mm
| ASTM D149 | 0.750 mm |