LNP™ THERMOCOMP™ OFC08
PPS(聚苯硫醚)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP OFC08 compound is based on Polyphenylene sulfide (PPS) resin containing 40% glass fiber. Added features of this grade include: High Modulus and Strength, Good Impact Strength and Ductility, Excellent Heat and Chemical Resistance, Good Electrical properties and Inherently FlameRetardant. It is also an Easy Flow grade with Good Flash Control. Applications of this grade include electric and electronic components, and various parts requiring high strength and high heat resistant.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 高强度耐热阻燃耐化学性良好流动性填充增强 | |||
成型方式 | 注塑 | |||
增强填充 | 40% 玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.66 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
315°C/5.0 kg | 15 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
315°C/5.0 kg | 25 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.3 % | Internal | |
横向(Across Flow) | 0.4~0.6 % | Internal | |
吸水率 | 0.01 % | ASTM D570 | 23°C/24hrs |
吸水率 | 0.02 % | ISO 62-1 | 23°C/24hrs |
吸水率 | 0.03 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.01 % | ISO 62-4 | 23°C/50% RH/24hrs |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 200 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 195 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 2.2 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
- | 295 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 295 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 15300 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 15000 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 16000 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 16000 Mpa | ISO 527 | 1 mm/min |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 55 kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 100 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-40℃ (-40℉) | 50 kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | 480 J/m | ASTM D4812 | |
23℃ (73℉) | 50 kJ/m² | ISO 180/1U | 80*10*4 |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 275 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)(4.6kg/cm²) | 275 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)(18.6kg/cm²) | 270 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
相对温度指数(RTI) | |||
冲击w/impact,- | 130 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 20 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
纵向(Flow) | 15 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 50 E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
横向(Across Flow) | 45 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | Min. |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.9 GHz | 4 - | Internal | |
耗散因数(DF) | |||
1.9 GHz | 42 E-4 | Internal |