DIC® FZ-2140-T3
PPS(聚苯硫醚)
迪爱生 (DIC)
产品描述
■ Product Summary: FZ-2140-T3 is a 40% glass fiber reinforced linear PPS compound with excellent mechanical properties and outstanding stability against coolants and hot water. Also its superior welding property gives flexibility to design of complexly
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度易焊接耐水解填充增强 | |||
| 颜色形状 | 黑色 | |||
| 增强填充 | 40% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.67 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.7 % | ISO 294-4 | |
吸水率 | 0.01 % | ISO 62 | 23˚C /24hrs. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 200 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-1/-2 | |
弯曲强度 | |||
- | 300 Mpa | ISO 178 | |
弯曲应变 | |||
断裂(brk) | 2.2 % | ISO 178 | |
弯曲模量 | 15000 Mpa | ISO 178 | |
拉伸模量 | 16000 Mpa | ISO 527-1/-2 | |
摩擦系数 | 0.35 - | Internal | dynamic, P=150kPa, V=0.3m/s, PPS vs. carbon steel |
摩擦系数 | 0.35 - | Internal | static, P=150kPa, V=0.3m/s, PPS vs. carbon steel |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 58 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 270 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 15 E-6/K | ISO 11359-2 | -50~50 ˚C |
纵向(Flow) | 15 E-6/K | ISO 11359-2 | 100~200 ˚C |
横向(Across Flow) | 40 E-6/K | ISO 11359-2 | -50~50 ˚C |
横向(Across Flow) | 105 E-6/K | ISO 11359-2 | 100~200 ˚C |
加工温度 | 300~340 °C | - | |
模具温度 | 130~150 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.74 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | IEC 60093 | |
介电常数(DK) | |||
1MHz | 4 - | IEC 60250 | |
耗散因数(DF) | |||
1MHz | 30 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 175 V | IEC 60112 | |
绝缘强度 | 26 kV/mm | IEC 60243-1 | t=1.0mm |