LNP™ STAT-KON™ OE006C1
PPS(聚苯硫醚)
沙特基础 (SABIC)
产品描述
LNP STAT-KON OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电填充增强 | |||
| 增强填充 | 30% 碳纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.44 g/cm³ | ASTM D792 | |
比重 | 1.45 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.08~0.1 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.7~0.9 % | ASTM D 955 | xflow, 24 hrs |
吸湿率 | 0.02 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.02 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 173 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 192 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 1.2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 1 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 269 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 263 Mpa | ISO 178 | |
弯曲模量 | 19900 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 19640 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 23540 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 21970 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 49 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 442 J/m | ASTM D4812 | |
23℃ (73℉) | 30 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 9 J | ASTM D3763 | |
多轴冲击 | 2 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 277 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 275 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 254 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 252 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 8 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) | 35 E-6/°C | ASTM D 696 | -30°C to 30°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2~1E+5 Ohm | ASTM D257 |