LNP™ STAT-KON™ OE006A
PPS(聚苯硫醚)
沙特基础 (SABIC)
产品描述
LNP STAT-KON* OE006A is a compound based on PPS - Branched resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电填充增强 | |||
| 增强填充 | 30% 碳纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.44 g/cm³ | ISO 1183 | |
密度 | 1.44 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.08 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.1 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.4 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 0.4 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.03 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.02 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 204 Mpa | ISO 527 | |
断裂(brk) | 210 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 1.1 % | ASTM D638 | |
断裂(brk) | 1 % | ISO 527 | |
弯曲强度 | |||
- | 304 Mpa | ASTM D790 | |
- | 311 Mpa | ISO 178 | |
弯曲模量 | 23510 Mpa | ASTM D790 | |
弯曲模量 | 24720 Mpa | ISO 178 | |
拉伸模量 | 32750 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 25450 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 1.6 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 1.38 - | ASTM D 3702 | Static COF |
磨损因数 | 857 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 49 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 437 J/m | ASTM D4812 | |
23℃ (73℉) | 28 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 3 J | ASTM D3763 | |
多轴冲击 | 1 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 7.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 8.7 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 39.6 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 40.8 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2~1E+6 Ohm | ASTM D257 |