LNP™ THERMOTUF™ OF006I
PPS(聚苯硫醚)
沙特基础 (SABIC)
产品描述
LNP THERMOTUF* OF006I is a compound based on PPS - Linear resin containing Glass Fiber. Added features of this material include: High Impact.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击填充增强 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.48 g/cm³ | ISO 1183 | |
密度 | 1.486 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.23 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.2 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.7 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 0.67 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.04 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 139 Mpa | ISO 527 | |
断裂(brk) | 143 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 2.4 % | ASTM D638 | |
断裂(brk) | 2 % | ISO 527 | |
弯曲强度 | |||
- | 207 Mpa | ASTM D790 | |
- | 212 Mpa | ISO 178 | |
弯曲模量 | 9790 Mpa | ASTM D790 | |
弯曲模量 | 10060 Mpa | ISO 178 | |
拉伸模量 | 10820 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 9820 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 170 J/m | ASTM D256 | |
23℃ (73℉) | 16 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 779 J/m | ASTM D4812 | |
23℃ (73℉) | 50 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 13 J | ASTM D3763 | |
多轴冲击 | 4 J | ISO 6603 |