Polytron P50B01LE is Black, 50% Long Glass Fiber Reinforced, Heat Stabilized,Reduced Emmision Behavior POLYPROPYLENE, The Glass Fibers are Chemically Coupled to the Polymer Matrix, The material is supplied in pellets that are typically 12mm in length. Fiber length is the length of the pellets. Typical applications include Structural Automotive Applications , For Passengers' compartment parts,Interior Applications
Regulations:
ROHS2: ROHS Compliance
SVHC: SVHC Compliance
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定低挥发VOC填充增强 | |||
| 添加助剂 | 化学偶联剂热稳定剂 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 长玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.1~0.15 % | Internal | 2mm |
横向(Across Flow) | 0.2~0.3 % | Internal | 2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 135 Mpa | ISO 527-2/1A | |
- | 100 Mpa | ISO 527-2/1A | AT 150C |
拉伸延伸率 | |||
断裂(brk) | 1.8 % | ISO 527-2/1A | |
断裂(brk) | 2.4 % | ISO 527-2/1A | AT 150C |
弯曲强度 | |||
- | 220 Mpa | ISO 178 | |
弯曲模量 | 12000 Mpa | ISO 178 | |
拉伸模量 | 12500 Mpa | ISO 527-2/1A | |
拉伸模量 | 8000 Mpa | ISO 527-2/1A | AT 70C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 22 kJ/m² | ISO 179-1/1eA | |
- | 25 kJ/m² | ISO 179-1/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-40℃ (-40℉) | 55 kJ/m² | ISO 179-1/1eU | |
- | 65 kJ/m² | ISO 179-1/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 158 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 157 °C | ISO 75 | |
熔融温度(Tm) | 168 °C | ISO 11357-3 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 3 mm | UL94 | |
FMVSS | 100 mm/min | FMVSS 302 | below |